A : 原料基本描述
| 暂无此原料描述部分[规格级别、外观颜色、用途说明都为空]！ |
B : 原料技术性能
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
--- |
ASTM D-792 |
1.57 |
--- |
| 阻燃性 |
--- |
UL 94 |
V-0 |
--- |
| 机械性能 |
拉伸强度 |
--- |
ASTM D-638 |
186(1900) |
MPa(Kg/cm2) |
| 伸长率 |
--- |
ASTM D-638 |
2.1 |
% |
| 弯曲强度 |
--- |
ASTM D-790 |
260(2650) |
MPa(Kg/cm2) |
| 拉伸模量 |
--- |
ASTM D-790 |
12(1.2) |
GPa(×105kg/cm2) |
|
|
--- |
|
|
| J/M(kg.cm/cm) |
| J/M(kg.cm/cm) | |
| 洛氏硬度 |
--- |
ASTM D-785 |
123 |
Rscal |
| 电气性能 |
体积电阻率 |
--- |
ASTM D-257 |
1×1016 |
Ω.cm |
| 介电常数 |
1MHz |
ASTM D-150 |
3.9 |
--- |
| 损耗因素 |
1MHz |
ASTM D-150 |
0.0014 |
--- |
| 介电强度 |
--- |
ASTM D-149 |
16 |
KV/mm |
| 加工性能 |
|
--- |
|
|
|
| 热 性 能 |
热膨胀系数 |
--- |
--- |
0.24(0.21) |
W/M.K(kcal/m.hr.℃) |
| 热变形温度 |
18.6kg/cm2 |
ASTM D-648 |
＞260 |
℃ |
| 线性热膨胀系数 |
--- |
Tosoh Method |
2.6 |
×10-51/K(×10-5cm/cm℃) | |
|