A : 原料基本描述
| 暂无此原料描述部分[规格级别、外观颜色、用途说明都为空]！ |
B : 原料技术性能
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
密度 |
--- |
ASTM D-792 |
1.14 |
g/cm3 |
| 吸水率 |
--- |
ASTM D-570 |
1.3-0.2 |
% |
| 饱和吸水率 |
--- |
ASTM D-570 |
8.5±0.5 |
% |
| 熔点 |
--- |
ASTM D-648 |
254 |
℃ |
| 物理性能 |
阻燃性 |
--- |
UL 94 |
V2/1.5mm |
Class/mm |
| 机械性能 |
拉伸强度 |
D |
ASTM D-638 |
85 |
MPa |
| 拉伸强度 |
C |
ASTM D-638 |
60 |
MPa |
| 断裂伸长率 |
D |
ASTM D-638 |
50-60 |
% |
| 断裂伸长率 |
C |
ASTM D-638 |
100 |
% |
| 弯曲强度 |
D |
ASTM D-790 |
115 |
MPa |
| 弯曲强度 |
C |
ASTM D-790 |
55 |
MPa |
| 弯曲模量 |
D |
ASTM D-790 |
2800 |
MPa |
| 弯曲模量 |
C |
ASTM D-790 |
1200 |
MPa |
| 冲击强度 |
D |
ASTM D-256 |
110 |
J/M |
| 冲击强度 |
C |
ASTM D-256 |
不断裂 |
J/M |
| 冲击强度（缺） |
D |
ASTM D-256 |
45 |
J/M |
| 冲击强度 |
D |
ASTM D-256 |
30 |
J/M |
| 蠕变模量 |
C |
DIN 53444 |
350 |
N/mm2 |
| 洛氏硬度 |
D |
ASTM D-785 |
R118 |
--- |
| 电气性能 |
介电常数 |
D |
ASTM D-696 |
3.5 |
--- |
| 介电损耗角 |
D |
ASTM D-150 |
0.025 |
--- |
| 介电损耗角 |
C |
ASTM D-150 |
0.2 |
--- |
| 介电强度 |
D |
ASTM D-150 |
120 |
KV/mm |
| 介电强度 |
C |
ASTM D-150 |
80 |
KV/mm |
| 体积电阻 |
D |
ASTM D-149 |
1015 |
Ω.cm |
| 体积电阻 |
C |
ASTM D-149 |
1012 |
Ω.cm |
| 表面电阻 |
D |
ASTM D-257 |
1013 |
Ω |
| 表面电阻 |
C |
ASTM D-257 |
1013 |
Ω |
| 热 性 能 |
线性热膨胀系数 |
D |
ASTM D-214 |
7-10 |
I/K10-5 |
| 热变形温度 |
264PSi |
ASTM D-785 |
100 |
℃ |
| 热变形温度 |
66PSi |
ASTM D-785 |
>220 |
℃ | |
|
 相 关 信 息 |
|
|
|
|
|
|
|
塑机样本 