PC/ABS CS701 南京立汉化学有限公司 |
|
发布日期:2006/3/28 776人次浏览 【 双击鼠标滚屏 】 |
|
A : 原料基本描述
| 规格级别： |
--- |
外观颜色： |
--- |
| 用途概述： |
汽车仪表盘摩托车缓冲板行车安全帽 |
| 备注说明： |
--- |
B : 原料技术性能
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
吸水率 |
--- |
ASTM D-570 |
- |
--- |
| 密度 |
--- |
ASTM D-792 |
1.12 |
g/cm3 |
| 机械性能 |
段裂拉伸强度 |
--- |
ASTM D-638 |
54 |
MPa |
| 段裂伸长率 |
--- |
ASTM D638 |
80 |
--- |
| 屈服弯曲强度 |
--- |
ASTM D790 |
85 |
MPa |
| 弯曲摸量 |
--- |
ASTM D-790 |
2300 |
MPa |
| 悬臂梁缺口冲击强度 |
--- |
ASTM D-256 |
450 |
J/M |
| 洛式硬度 |
--- |
--- |
R108 |
--- |
| 电气性能 |
体积电阻 |
--- |
ASTM D-257 |
- |
0hm.cm |
| 表面电阻 |
--- |
ASTM D-257 |
- |
0hm |
| 介电强度 |
--- |
ASTM D-149 |
20/- |
KV/mm |
| 加工性能 |
饱和吸水率 |
--- |
ASTM D-570 |
- |
--- |
| 注塑成型温度范围 |
--- |
--- |
240-280 |
℃ |
| 烘干温度/时间 |
--- |
--- |
- |
℃/hr |
| 线形成型收缩率 |
--- |
ASTM D-955 |
0.006 |
mm/mm |
| 熔体流动速率 |
--- |
ASTM D-1238 |
22 |
g/10min |
| 热 性 能 |
熔点 |
--- |
--- |
- |
℃ |
| 线形热膨胀系数 |
10-5cm/cm |
ASTM D-696 |
HB |
.℃ |
| 热变形温度 |
0.45MPa |
ASMT D-648 |
- |
℃ |
| 热变形温度 |
1.81MPa |
ASTM D-648 |
100 |
℃ | |
|