性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
基本性能 |
比重 |
--- |
D792 |
1.2 |
--- |
相比于流动态的膜收缩,3.2-mm(0.125in./in.),厚度 |
--- |
D955 |
0.002-0.006mm/mm(0.002-0.006in./in.) |
--- |
物理性能 |
光雾 |
--- |
D1003 |
0.3% |
--- |
一般透过率 |
--- |
D1003 |
89% |
--- |
总透过率 |
--- |
D1003 |
91% |
--- |
机械性能 |
|
--- |
|
47MPa(6900 psi) |
51MPa(7400 psi) | |
--- |
|
--- |
|
|
--- |
挠曲模量 |
--- |
D790 |
2000MPa(2.9×105 psi) |
--- |
挠曲屈服强度 |
--- |
D790 |
69MPa(10000 psi) |
--- |
洛氏硬度 |
R刻度 |
D785 |
103 |
--- |
悬梁式冲击强度 |
@23℃(73?H) |
@-40℃(-40?H) | |
|
|
80 J/m(1.5 ft bf/in) |
40 J/m(0.7 ft bf/in) | |
--- |
冲击强度 |
@23℃(73�H) |
@-40℃(-40�H) | |
|
|
NB J/m(NB ft bf/in) |
NB J/m(NB ft bf/in) | |
--- |
抗冲击(穿孔),能量@最大负荷 |
@23℃(73�H) |
@-40℃(-40�H) | |
--- |
|
42 J(31 ft bf) |
48 J/m(35 ft bf) | |
--- |
|
--- |
|
|
--- |
|
--- |
|
|
--- |
拉伸模量 |
--- |
ISO 527 |
1800MPa |
--- |
挠曲模量 |
--- |
ISO 178 |
1850MPa |
--- |
屈挠强度 |
--- |
ISO 178 |
65MPa |
--- |
|
|
|
|
--- |
加工性能 |
干燥温度 |
--- |
--- |
70℃(160�H) |
--- |
干燥时间 |
--- |
--- |
6小时 |
--- |
加工熔融温度 |
--- |
--- |
230-280℃(450-530�H) |
--- |
塑膜温度 |
--- |
--- |
15-30℃(60-80�H) |
--- |
热 性 能 |
挠曲温度 |
0.455MPa(66 psi) |
1.82MPa(264 psi) | |
--- |
|
|
--- |