POM 900 美国杜邦公司 |
|
发布日期:2006/3/28 701人次浏览 【 双击鼠标滚屏 】 |
|
A : 原料基本描述
| 暂无此原料描述部分[规格级别、外观颜色、用途说明都为空]！ |
B : 原料技术性能
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
密度 |
--- |
ASTM D-792 |
1.42 |
--- |
| 物理性能 |
吸水量 |
24hrs浸泡+73�H(+23℃) |
ASTM D-570 |
0.25 |
% |
| 吸水量 |
Equil.50%R.h.+73�H(+23℃) |
ASTM D-570 |
0.22 |
% |
| 吸水量 |
浸泡均衡点+73�H(+23℃) |
ASTM D-570 |
0.90 |
% |
| 机械性能 |
洛氏硬度 |
--- |
ASTM D-785 |
M94,R120 |
--- |
| 摩擦系数 |
+73�H(+23℃)静态 |
ThrustWasherTest3 |
0.20 |
--- |
| 摩擦系数 |
+73�H(+23℃)动态 |
ThrustWasherTest3 |
0.35 |
--- |
| 断裂时之拉力伸张度 |
-68�H(-55℃) |
ASTM D-638 |
10 |
% |
| 断裂时之拉力伸张度 |
+73�H(+23℃) |
ASTM D-638 |
25 |
% |
| 断裂时之拉力伸张度 |
+158�H(+70℃) |
ASTM D-638 |
180 |
% |
| 断裂时之拉力伸张度 |
+212�H(+100℃) |
ASTM D-638 |
>260 |
% |
| 断裂时之拉力伸张度 |
+250�H(+122℃) |
ASTM D-638 |
>260 |
% |
| 伸张强度 |
-68�H |
ASTM D-638 |
14.7 |
MPsi |
| 伸张强度 |
-55℃ |
ASTM D-638 |
101 |
MPa |
| 伸张强度 |
+73�H |
ASTM D-638 |
10.0 |
MPsi |
| 伸张强度 |
+23℃ |
ASTM D-638 |
68.9 |
MPa |
| 伸张强度 |
+158�H |
ASTM D-638 |
6.9 |
MPsi |
| 伸张强度 |
+70℃ |
ASTM D-638 |
47.5 |
MPa |
| 伸张强度 |
+212�H |
ASTM D-638 |
5.2 |
MPsi |
| 伸张强度 |
+100℃ |
ASTM D-638 |
35.9 |
MPa |
| 伸张强度 |
+250�H |
ASTM D-638 |
3.8 |
MPsi |
| 伸张强度 |
+122℃ |
ASTM D-638 |
26.2 |
MPa |
| 弹性系数 |
+73�H |
ASTM D-638 |
450 |
MPsi |
| 弹性系数 |
+23℃ |
ASTM D-638 |
3100 |
MPa |
| 剪力 |
+23℃ |
ASTM D-732 |
65.5 |
MPa |
| 挠曲系数 |
-68�H |
在25℃下 |
600 |
MPsi |
| 挠曲系数 |
-55℃ |
在25℃下 |
4140 |
MPa |
| 挠曲系数 |
+73�H |
在25℃下 |
430 |
MPsi |
| 挠曲系数 |
+23℃ |
在25℃下 |
2960 |
MPa |
| 挠曲系数 |
+158�H |
在25℃下 |
240 |
MPsi |
| 挠曲系数 |
+70℃ |
在25℃下 |
1655 |
MPa |
| 挠曲系数 |
+212�H |
在25℃下 |
140 |
MPsi |
| 挠曲系数 |
+100℃ |
在25℃下 |
965 |
MPa |
| 挠曲系数 |
+250�H |
在25℃下 |
90 |
MPsi |
| 挠曲系数 |
+122℃ |
在25℃下 |
620 |
MPa |
| 弯曲降服强度 |
+73�H |
ASTM D-790 |
14.0 |
MPsi |
| 弯曲降服强度 |
+23℃ |
ASTM D-790 |
96.5 |
MPa |
| 压缩应力 |
+73�H@1%ASTM D-ef. |
ASTM D-695 |
5.0 |
MPsi |
| 压缩应力 |
+23℃@1%ASTM D-ef. |
ASTM D-695 |
34.5 |
MPa |
| 压缩应力 |
+73�H@10%ASTM D-ef. |
ASTM D-695 |
17.6 |
MPsi |
| 压缩应力 |
+23℃@10%ASTM D-ef. |
ASTM D-695 |
121 |
MPa |
| 负载下之变形 |
2000psi@+122�H(14Mpa@50℃) |
ASTM D-621 |
0.5 |
% |
| 弯曲疲劳忍耐限度 |
+73�H |
ASTM D-671 |
4.6 |
MPsi |
| 弯曲疲劳忍耐限度 |
+23℃ |
ASTM D-671 |
31.7 |
MPa |
| IZOD冲击强度 |
-40�H |
ASTM D-256 |
1.0 |
ft.lb/in |
| IZOD冲击强度 |
40℃ |
ASTM D-256 |
53.4 |
j/m |
| IZOD冲击强度 |
+73�H |
ASTM D-256 |
1.3 |
ft.lb/in |
| IZOD冲击强度 |
+23℃ |
ASTM D-256 |
69.4 |
j/m |
| 拉力冲击抵抗力 |
+73�H |
ASTM D-1822 |
70 |
ft.lb/in2 |
| 拉力冲击抵抗力 |
+23℃ |
ASTM D-1822 |
150 |
kj/m2 |
| 无切口冲击程度 |
+73�H |
ASTM D-256 |
16 |
ft.lb/in |
| 无切口冲击程度 |
+23℃ |
ASTM D-256 |
850 |
j/m |
| 线性热膨胀系数 |
+85 to +140�H |
ASTM D-696 |
6.8 |
10-5in/in.�H |
| 热传导系数 |
BTU-in/hr |
--- |
2.6 |
--- |
| 扩散因数 |
+73�H(+23℃)106Hz |
ASTM D-150 |
0.005 |
--- |
| 电气性能 |
绝缘系数 |
+73�H(+23℃)102to106Hz |
ASTM D-150 |
3.7 |
--- |
| 电阻系数 |
+73�H(+23℃)0.2%H2O |
ASTM D-257 |
1015 |
ohm-cm |
| 电弧抵抗力 |
120mil(3.1mm) |
ASTM D-495 |
220no tracking |
Sec. |
| 绝缘强度 |
Short Time,90 mils |
ASTM D-149 |
500 |
V/mil |
| 绝缘强度 |
Short Time,2.3mm |
ASTM D-149 |
19.7 |
MV/m |
| 热 性 能 |
可燃烧性 |
--- |
UL-94 |
94HB |
--- |
| 热传导系数 |
W/mk |
--- |
0.37 |
--- |
| 线性热膨胀系数 |
+104 to +150℃ |
ASTM D-696 |
14.9 |
10-5m/m.℃ |
| 线性热膨胀系数 |
+60 to +104℃ |
ASTM D-696 |
13.7 |
10-5m/m.℃ |
| 线性热膨胀系数 |
+220 to +300�H |
ASTM D-696 |
8.3 |
10-5in/in.�H |
| 线性热膨胀系数 |
-40 to +29℃ |
ASTM D-696 |
10.4 |
10-5m/m.℃ |
| 线性热膨胀系数 |
+29 to +60℃ |
ASTM D-696 |
12.2 |
10-5m/m.℃ |
| 线性热膨胀系数 |
+140 to +220�H |
ASTM D-696 |
7.6 |
10-5in/in.�H |
| 熔点 |
--- |
ASTM D-2133 |
347 |
�H |
| 熔点 |
--- |
ASTM D-2133 |
175 |
℃ |
| 线性热膨胀系数 |
-40 to +85�H |
ASTM D-696 |
5.8 |
10-5in/in.�H |
| 热变形温度 |
0.5MPa |
ASTM D-648 |
172 |
℃ |
| 热变形温度 |
1.8MPa |
ASTM D-648 |
136 |
℃ |
| 热变形温度 |
66psi |
ASTM D-648 |
342 |
�H |
| 热变形温度 |
264psi |
ASTM D-648 |
277 |
�H | |
|