B : 原料技术性能
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
比重 |
--- |
ASTM D-792 |
1.2 |
--- |
| 熔体流动速率 |
300℃ 1.2kg |
ISO 1133(ASTM D-1238) |
5 |
g/10分 |
| 物理性能 |
光线透过率 |
3mm厚 |
ASTM D-1003 |
85-89 |
% |
| 吸水率 |
23℃水中24h |
ASTM D-570 |
0.23 |
% |
| 机械性能 |
引张降伏强度 |
--- |
ISO R-527(ASTM D-638) |
64(650) |
MPa(Kg/cm2) |
| 引张破坏强度 |
--- |
ISO R-527(ASTM D-638) |
78(800) |
MPa(Kg/cm2) |
| 引张弹性率 |
--- |
ISO R-527(ASTM D-638 |
2300(23500) |
MPa(Kg/cm2) |
| 引张破坏伸率 |
--- |
ISO R-527(ASTM D-638 |
ISO R-527(ASTM D-638 |
% |
| 挠曲强度 |
--- |
ISO 178(ASTM D-790) |
95(970) |
MPa(Kg/cm2) |
| 挠曲弹性率 |
--- |
ISO 178(ASTM D-790) |
2350(24000) |
MPa(Kg/cm2) |
| IZOD冲击强度 |
4mm with notch 3.2mm with notch |
ISO 180(ASTM D-256) |
80(100) |
KJ/m2(kg・cm/cm2) |
| 洛氏硬度 |
--- |
ISO 2039-2(ASTM D-785) |
R120(M75) |
--- |
| 电气性能 |
绝缘破坏电压 |
1.6mm厚 |
ASTM D-149 |
30 |
Kv/mm |
| 体积固有抵抗 |
--- |
ASTM D-257 |
1016＜ |
Ω・cm |
| 诱电率 |
--- |
ASTM D-150 |
2.91(2.85) |
60Hz(106Hz) |
| 诱电正接 |
60Hz(106Hz) |
ASTM D-150 |
6.6×10-4(9.2×10-3) |
--- |
| 耐电弧性 |
--- |
ASTM D-495 |
110 |
Sec |
| 热 性 能 |
成形收缩率 |
--- |
ASTM D-955 |
0.5-0.7 |
% |
| 泰伯磨耗量 |
1,000round |
ASTM D-1044 |
12 |
mg |
| 热变形温度 |
1.8Mpa 18.6kg/cm2 |
ISO 75(ASTM D-648) |
135 |
℃ |
| 维卡软化点 |
--- |
ISO 306 |
150 |
℃ |
| 线膨胀系数 |
--- |
ASTM D-696(ASTM D-695) |
6.5 |
×10-5cm/cm/℃ | |
|