A : 原料基本描述
| 规格级别： |
--- |
外观颜色： |
--- |
| 用途概述： |
汽车仪表盘摩托车缓冲板行车安全帽 |
| 备注说明： |
--- |
B : 原料技术性能
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
熔体流动速率 |
--- |
ASTM D-1238 |
20 |
g/10min |
| 物理性能 |
密度 |
--- |
ASTM D-792 |
1.14 |
g/cm3 |
| 吸水率 |
--- |
ASTM D-570 |
- |
--- |
| 机械性能 |
断裂拉伸强度 |
--- |
ASTM D-638 |
58 |
MPa |
| 断裂伸长率 |
--- |
ASTM D-638 |
120 |
--- |
| 屈服弯曲强度 |
--- |
ASTM D-790 |
100 |
MPa |
| 弯曲摸量 |
--- |
ASTM D-790 |
2400 |
MPa |
| 悬臂梁缺口冲击强度 |
--- |
ASTM D-256 |
500 |
J/M |
| 洛式硬度 |
--- |
--- |
R110 |
--- |
| 电气性能 |
体积电阻 |
--- |
ASTM D-257 |
- |
0hm.cm |
| 表面电阻 |
--- |
ASTM D-257 |
- |
0hm |
| 介电强度 |
--- |
ASTM D-149 |
20/- |
KV/mm |
| 加工性能 |
饱和吸水率 |
--- |
ASTM D-570 |
- |
--- |
| 注塑成型温度范围 |
--- |
--- |
240-280 |
℃ |
| 烘干温度/时间 |
--- |
--- |
- |
℃/hr |
| 形成型收缩率 |
--- |
ASTM D-955 |
0.006 |
mm/mm X |
| 热 性 能 |
熔点 |
--- |
--- |
- |
℃ |
| 线形热膨胀系数 |
10-5cm/cm.℃ |
ASTM D-696 |
HB |
℃ |
| 热变形温度 |
0.45MPa |
ASTM D-648 |
- |
℃ |
| 热变形温度 |
1.81MPa |
ASTM D-648 |
108 |
℃ | |
|