PC 200-03 美国陶氏化学公司 |
|
发布日期:2006/3/28 2514人次浏览 【 双击鼠标滚屏 】 |
|
A : 原料基本描述
| 暂无此原料描述部分[规格级别、外观颜色、用途说明都为空]！ |
B : 原料技术性能
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
熔融指数 |
--- |
ASTM D-1238 |
4 |
g/10min |
| 密度 |
--- |
ASTM D-792 |
1200 |
kg/cm3 |
| 吸水率 |
23℃，24时间 |
ASTM D-570 |
0.15 |
% |
| 物理性能 |
模缩率 |
--- |
ASTM D-955 |
0.005-0.007 |
mm/min |
| 折射率 |
--- |
ASTM D-542 |
1.586 |
--- |
| 透光率 |
--- |
ASTM D-1003 |
89 |
% |
| 雾度 |
--- |
ASTM D-1003 |
1 |
% |
| 机械性能 |
拉伸屈服强度 |
--- |
ASTM D-638 |
60 |
MPa |
| 拉伸断裂强度 |
--- |
ASTM D-638 |
72 |
MPa |
| 拉伸断裂伸长率 |
--- |
ASTM D-638 |
150 |
% |
| 拉伸模量 |
--- |
ASTM D-638 |
2480 |
MPa |
| 弯曲强度 |
--- |
ASTM D-790 |
96 |
MPa |
| 弯曲模量 |
23℃ |
ASTM D-790 |
2410 |
MPa |
| 缺口冲击强度 |
23℃ |
ASTM D-256 |
950 |
J/m |
| 冲击强度 |
--- |
ASTM D-256 |
未断裂 |
--- |
| 洛氏硬度M |
--- |
ASTM D-785 |
74 |
--- |
| 洛氏硬度R |
--- |
ASTM D-785 |
118 |
--- |
| 电气性能 |
介电强度 |
--- |
ASTM D-149 |
17 |
Kv/mm |
| 热 性 能 |
耗散因子 |
60HZ |
ASTM D-150 |
0.001 |
--- |
| 维卡软化温度 |
--- |
ASTM D-1525 |
151 |
℃ |
| 线性热收缩率 |
--- |
ASTM D-696 |
68×10-6 |
mm/mm/℃ |
| 热变形温度 |
0.45MPa |
ASTM D-648 |
146 |
--- |
| 热变形温度 |
1.82MPa |
ASTM D-648 |
143 |
℃ |
| 热变形温度 |
1.82MPa |
ASTM D-648 |
132 |
℃ |
| 体积电阻率 |
--- |
ASTM D-257 |
2.0×1017 |
Ω.cm |
| 阻燃性 |
--- |
UL 94 |
HB |
--- |
| 平均燃烧程度 |
--- |
ASTM D-635 |
25 |
mm |
| 其它性能 |
氧指数 |
--- |
ASTM D-2863 |
26 |
% | |
|
 相 关 信 息 |
|
|
|
|
|
|
|
 |
|